N700

Application Segments

Additive Manufacturing Application

Melting Route

VIGA

Product Description

BÖHLER N700 AMPO (17-4 PH) is a precipitation hardening nickel martensitic steel. Thanks to its alloying system, this material has excellent corrosion resistance. Can be printed very easily without additional heating of the platform or chamber and, after solution annealing and aging, hardens up to approx. 40 HRC.

Property Features

Particle size distribution 15 – 45 µm:
D10[µm]                            18 – 24
D50[µm]                            29 – 35
D90[µm]                            42 – 50
Apparent density*            ≥ 3.4 g/cm³
Measurement of particle size distribution according to ISO 13322-2 (Dynamic image analysis methods);
* Measurement of apparent density is based on ASTM B964 resp. DIN EN ISO 3923-1 and relates to our typical measured values

 

Achievable mechanical properties of printed part after heat treatment:
Tensile strength (Rm)                            1150 ± 150 MPa
Yield strength (RP₀,₂)                            1050 ± 150 MPa
Elongation (%)                                         18 ± 3
Hardness                                                 36 to 43 HRc
Impact toughness (ISO V)                          75 – 230 J

 

Particle size distribution 45 – 90 µm:
Details on request

Technical Specifications

Material Numbers


1.4542 17-4 PH X5CrNiCuNb16-4 S17400


Chemical Composition

Chemical composition (average %)
0.04 16.25 4.00 4.00 0.34

Available product shapes

  • 15 - 45 μm
  • 45 - 90 μm